CM2000 Landtek
Rs.6,000/-
Viewed 2715 times
Categories Cart Account Search Recent View Go to Top
All Categories ×
- Anemometer
- Barcol Impressor
- Coating Thickness Gauge
- Color Meter
- Dew Point Meter
- Digital Force Gauge
- Digital Gauss Meter
- Elevator Speed Limiter Speedometer
- Featured Products
- Foam Hardness Tester
- Fruit Hardness Tester
- Gloss Meter
- Hardness Tester
- Humidity Meter
- Latest Products
- Leeb Hardness Tester
- Lux Meter
- Moisture Meter
- Pencil Hardness Tester
- Popular Products
- Reflectance Meter (Cryptometer)
- Sand Mould Surface Hardness Tester
- Shore Hardness Tester
- Sonic Belt Tension Tester
- Sound Level Calibrator
- Sound Level Meter
- Stroboscope
- Surface Roughness Tester
- Tachometer
- Temperature Meter
- Temperature Probe, & pH Meter
- Tension Tester
- Textile Hardness Tester
- Ultrasonic Leakage Detector
- Ultrasonic Thickness Gauge
- Ultrasonic Transmitter
- Universal Accessories
- Vibration Calibrator
- Vibration Meter
- Water Activity Meter
- Wet Film Comb
- Whiteness Meter
- Window Tint Meter
- Wood Density Tester
Shopping Cart ×
Your shopping cart is empty!
Search ×
Recent View Products ×
Product Description
Used for checking the thickness coating of wet paint, enamel lacquer,adhensive , architectural coating, color coating, varnish, chemical industry,or other coating that has been applied to a smooth surface.
Specifications
Standards | GB/T1764-79 GB/T134522-92 ISO2808-74 | |
Range | 25~2032μm / 1~80mil | |
Values | 25, 51, 75, 102, 127, 152, 178, 203, 229, 254, 279, 305, 356, 406, 457, 508, 559, 610, 660, 711, 762, 889, 1016, 1143, 1270, 1397, 1524, 1651, 1778, 2032µm | |
1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 14, 16, 18, 20, 22, 24, 26, 28, 30, 35, 40, 45, 50, 55, 60, 65, 70, 80mil |
Measuring Procedure
1. Select appropriate comb according to approximate known thickness.
2. Hold comb perpendicular to surface coating to be measured.
3. Press into coating until the comb stands square on substrate.
4. Wet film thickness is between the highest step which is coated and the next (higher) step which remains uncoated.